EXQUISITE INTERNATIONAL all the time insist on selecting durable polyester fabric as the core and environmental new PVC as material as well as special unique formulations, thus makes the belt work life plus 5%-15%, it is outstandingly reducing the user's cost and increase the productivity rate 10%-20%, guarantee user's projects. |
|
|
|
|
| GENERAL CHARACTERISTICS |
|
|
*anti-oil anti-grease *moisture proof *low extension *anti-corrosion *Non-toxic, non-odorless
*high tensile strength *anti high and low temperature *Strong bonded, no shedding |
|
|
|
|
|
|
|
|
| BELT Structure |
|
|
|
| No. of Ply: | 2 | Minimum Pulley Diameters |
|
| Fabric Features | 2 ply fabric, 2 ply pvc | Positive Operation: 50mm |
|
| -Top Surface | PVC fabric | Reverse Operation: 70mm |
|
| -Colour | White |
|
|
| -Thickness | 1.0 mm | Conveyor Frame Characteristics |
|
| Hardness | 72 Shore A | Trundle Bed: Yes |
|
| Surface | Q Struc | Metal Groove: Yes |
|
| Bottom Surface | Fabric | Plate Roller to Support: Yes |
|
| Total Thickness | 2.0 mm | Inverted Wheel to Support: NO |
|
| Weight | 2.3 kg/㎡ | Special Mixed Inverted Wheel Groove: NO |
|
| Anti-static | Yes | Reverse Slide: Yes |
|
| Maximum width | 3500mm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Belt Strength |
| Joint Methods |
|
| fracture tension: 240 daN / cm | hot Melt: FOF |
|
| recommended maximum working tension: 12 daN / cm | buckle: K1 B2/Z or Inox |
|
| working tension under extension rate of 1%: 10 daN / cm |
|
|
|
|
|
|
|
|
|
|
| Operating Temperature: -20℃ to 80℃ | Bottom Cover Friction Coefficient |
|
temperature± 30% influenced by working time,
weight of material, different factors in the environment | Stainless steel, surface: 0.24 |
|
| Stainless steel, semi-glossy: 0.24 |
|
| Stainless steel, heat lamination surface: 0.25 |
|
| Scroll Plate: 0.23 |
|
|
| Glossy plastic board: 0.28 |
|
|
|
|
|
| Special Executions |
The test data under the environment: + 25 ℃, 70% relative humidity. And in other circumstances, the data are subject to change, EXQUISITE INTL does not specify more.
|